Crystallization kinetics of amorphous alumina–zirconia–silica ceramics
- 1.
SYSNO ASEP 0329728 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Crystallization kinetics of amorphous alumina–zirconia–silica ceramics Překlad názvu Kinetika krystalizace amorfní keramiky obsahující Al2O3-ZrO2-SiO2 Tvůrce(i) Chráska, Tomáš (UFP-V) RID, ORCID
Hostomský, Jiří (UACH-T)
Klementová, Mariana (UACH-T) RID, SAI, ORCID
Dubský, Jiří (UFP-V) RIDZdroj.dok. Journal of the European Ceramic Society. - : Elsevier - ISSN 0955-2219
Roč. 29, č. 15 (2009), s. 3159-3165Poč.str. 7 s. Forma vydání web - web Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova Nanocomposites ; Al2O3 ; ZrO2 ; SiO2 ; Solid-state reaction Vědní obor RIV JH - Keramika, žáruvzdorné materiály a skla CEP KAN300430651 GA AV ČR - Akademie věd CEZ AV0Z20430508 - UFP-V (2005-2011) AV0Z40320502 - UACH-T (2005-2011) UT WOS 000270162100007 DOI doi:10.1016/j.jeurceramsoc.2009.05.020 Anotace Crystallization kinetics of amorphous alumina–zirconia–silica ceramics was studied by nonisothermal differential scanning calorimetry (DSC). Different amorphous materials were produced by plasma spraying of near-eutectic Al2O3–ZrO2–SiO2 mixtures. Phase composition and microstructure of the amorphous materials and nanocrystalline products were analyzed. All of the investigated materials show an exothermic peak between 940 and 990 C in the DSC experiments. The activation energies calculated from DSC traces decrease with increasing SiO2 concentration. Values of the Avrami coefficients together with results of the microstructural observations indicate that tetragonal zirconia crystallization from materials containing more than 10 wt.% SiO2 proceeds by a diffusion-controlled mechanism with nucleation occurring predominantly at the beginning of the process. Pracoviště Ústav fyziky plazmatu Kontakt Vladimíra Kebza, kebza@ipp.cas.cz, Tel.: 266 052 975 Rok sběru 2010
Počet záznamů: 1