Direct transmission electron microscopy observations of martensitic transformations in Ni-rich NiTi single crystals during in situ cooling and straining
- 1.
SYSNO ASEP 0324851 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Direct transmission electron microscopy observations of martensitic transformations in Ni-rich NiTi single crystals during in situ cooling and straining Překlad názvu Přímá pozorování martenzitických transformací metodou transmisní elektronové mikroskopie Ni-bohatých monokrystalů NiTi během in-situ chlazení a deformace Tvůrce(i) Kröger, A. (DE)
Dziaszyk, S. (DE)
Frenzel, J. (DE)
Somsen, Ch. (DE)
Dlouhý, Antonín (UFM-A) RID, ORCID
Eggeler, G. (DE)Zdroj.dok. Materials Science and Engineering A Structural Materials Properties Microstructure and Processing. - : Elsevier - ISSN 0921-5093
Roč. 481, Sp. Iss. (2008), s. 452-456Poč.str. 5 s. Akce ESOMAT 2006 Datum konání 10.09.2006-15.09.2006 Místo konání Bochum Země DE - Německo Typ akce EUR Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova In situ TEM ; NiTi single crystal ; Martensitic transformations Vědní obor RIV BM - Fyzika pevných látek a magnetismus CEZ AV0Z20410507 - UFM-A (2005-2011) UT WOS 000255716100093 DOI 10.1016/j.msea.2007.02.169 Anotace We investigate martensitic transformations using transmission electron microscopy (TEM) in compression aged Ni-rich NiTi single crystals with one family of Ni4Ti3 precipitates. Differential scanning calorimetry (DSC) investigations show that a threestep martensitic transformation (three DSC peaks on cooling from the high temperature regime) can be observed for aging times of 4 ks. In situ cooling TEM investigations reveal that the first peak on cooling is associated with a transformation from B2 to R-phase, starting from all precipitate/matrix interfaces. On further cooling, the B19'-phase appears and grows along precipitate/matrix interfaces (second step). With further decreasing temperature, the remaining R-phase between the precipitates transforms to B19' (third peak). In situ TEM straining experiments of B2 above the martensitic start temperature reveal that first some microstructural regions directly transform in microscopic burst like events from B2 to B19'. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2009