Počet záznamů: 1
Microstructure and physical properties of mechanically alloyed Fe-Mo powder
- 1.
SYSNO ASEP 0323821 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Ostatní články Název Microstructure and physical properties of mechanically alloyed Fe-Mo powder Překlad názvu Mikrostruktura a fyzikální vlastnosti mechanicky legovaných Fe-Mo prášků Tvůrce(i) Jirásková, Yvonna (UFM-A) RID, ORCID
Zábranský, Karel (UFM-A)
Turek, Ilja (UFM-A) RID, ORCID
Buršík, Jiří (UFM-A) RID, ORCID
Jančík, D. (CZ)Zdroj.dok. Journal of Alloys and Compounds. - : Elsevier - ISSN 0925-8388
Roč. 477, - (2009), s. 55-61Poč.str. 7 s. Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova Nanostructured materials ; Mechanical alloying ; Microstructure ; Magnetic measurements ; Mössbauer spectroscopy Vědní obor RIV BM - Fyzika pevných látek a magnetismus CEP GA202/05/2111 GA ČR - Grantová agentura ČR GD106/05/H008 GA ČR - Grantová agentura ČR CEZ AV0Z20410507 - UFM-A (2005-2011) DOI 10.1016/j.jallcom.2008.11.006 Anotace Solid state reactions in Fe74Mo26 powder mixture induced by mechanical alloying (MA) are followed by 57Fe Mössbauer spectroscopy supported by additional experimental methods. It is established that a bcc-Fe(Mo) solid solution with an enhanced Mo content substantially exceeding the equilibrium solubility limit, a bcc-Mo(Fe) solid solution, and an amorphous and/or highly defected phase have been formed during the MA. The mean particle size of 100 nm is obtained at the end of milling process. Surface regions of the particles are formed by the amorphous phase containing also iron grains smaller than 20 nm, as proved by transmission electron microscopy and selective area electron diffraction. A varying composition of FeMo powder samples and grain refinement are reflected in changes of hyperfine interactions and macroscopic magnetic characteristics. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2009
Počet záznamů: 1