The effect of polyethylene addition on the morphology of polystyrene/polyamide blends

  1. 1.
    0330036 - ÚMCH 2010 RIV US eng J - Článek v odborném periodiku
    Fortelný, Ivan - Lapčíková, Monika - Mikešová, Jana - Jůza, Josef
    The effect of polyethylene addition on the morphology of polystyrene/polyamide blends.
    [Vliv přídavku polyethylenu na morfologii směsí polystyren/polyamid.]
    Journal of Polymer Science. Part B, Polymer Physics. Roč. 47, č. 21 (2009), s. 2158-2170. ISSN 0887-6266
    Grant CEP: GA ČR GA106/06/0729
    Výzkumný záměr: CEZ:AV0Z40500505
    Klíčová slova: phase structure * polyamide * polyethylene
    Kód oboru RIV: CD - Makromolekulární chemie
    Impakt faktor: 1.586, rok: 2009

    The effect of a small admixture of high-density polyethylene (HDPE) with a high or low viscosity to polystyrene/polyamide (PS/PA) blends of various compositions was studied. PS/PA blends with composition near 50/50 form sheet-like or fiber-like morphology at mixing that passes to the cocontinuous structure during compression molding. Ternary PS/PA/HDPE blends with PS/PA ratio about 50/50 show similar behavior.

    Studovali jsme vliv malého přídavku vysokohustotního polyethylenu (HDPE) s vysokou nebo nízkou viskozitou na morfologii směsí polystyren/polyamid (PS/PA) o různém složení. Směsi PS/PA se složením blízkým 50/50 vytvářejí při míchání destičkovou nebo vláknitou strukturu která během lisování přechází na strukturu kokontinuální. Ternární směsi PS/PA/HDPE s poměrem PS/PA okolo 50/50 vykazují podobné chování.
    Trvalý link: http://hdl.handle.net/11104/0175909

     
     