Multi-parameter crack tip stress state description for estimation of fracture process zone extent in silicate composite WST specimens
SYS 0422440 LBL 02226^^^^^2200397^^^450 005 20240103203607.8 017 70
$a 10.3221/IGF-ESIS.25.11 $2 DOI 100 $a 20140210d m y slo 03 ba 101 0-
$a eng $d eng 102 $a IT 200 1-
$a Multi-parameter crack tip stress state description for estimation of fracture process zone extent in silicate composite WST specimens 215 $a 10 s. 463 -1
$1 001 cav_un_epca*0353149 $1 011 $a 1971-8993 $1 200 1 $a Frattura ed Integrita Strutturale $v Roč. 7, č. 25 (2013), s. 69-78 $1 210 $c Gruppo Italiano Frattura 610 0-
$a Near-crack tip fields 610 0-
$a Williams series 610 0-
$a higher-order terms 610 0-
$a stress field approximation 610 0-
$a wedge splitting test 610 0-
$a fracture process zone 700 -1
$3 cav_un_auth*0053334 $a Veselý $b V. $y CZ $4 070 701 -1
$3 cav_un_auth*0287329 $a Sobek $b J. $y CZ $4 070 701 -1
$3 cav_un_auth*0268290 $a Šestáková $b L. $y CZ $4 070 701 -1
$3 cav_un_auth*0220630 $a Frantík $b P. $y CZ $4 070 701 -1
$3 cav_un_auth*0101322 $a Seitl $b Stanislav $i Vysokocyklová únava $j High cycle fatigue $p UFM-A $w High Cycle Fatigue Group $4 070 $T Ústav fyziky materiálů AV ČR, v. v. i.
Počet záznamů: 1