Coalescence during annealing of quiescent immiscible polymer blends

0358512 - ÚMCH 2012 RIV US eng J - Článek v odborném periodiku
Dimzoski, Bojan - Fortelný, Ivan - Šlouf, Miroslav - Nevoralová, Martina - Michálková, Danuše - Mikešová, Jana
Coalescence during annealing of quiescent immiscible polymer blends.
E-Polymers. -, 011 (2011), s. 1-12. ISSN 1618-7229. E-ISSN 1618-7229
Grant CEP: GA AV ČR IAA200500903
Výzkumný záměr: CEZ:AV0Z40500505
Klíčová slova: coalescence * polymer blends * annealing
Kód oboru RIV: BJ - Termodynamika
Impakt faktor: 0.515, rok: 2011
http://www.e-polymers.org/journal/papers/bdimzoski_010311.pdf

Coalescence during annealing of quiescent immiscible polymer blends, containing polypropylene matrix and different amount of ethylene-propylene copolymer (EPR) as dispersed phase, was studied. Comparison of experimental results with available coalescence theories revealed that changes in the phase structure after 20 min annealing can be precisely estimated using the approximate theory of coalescence induced by van der Waals forces and considering drainage of the matrix film between spherical droplets. All results evidenced growth of the EPR droplet size with the annealing time and temperature; increase in the content of dispersed phase contributed to higher growth rate of the dispersed phase, more pronounced at the coalescence origin. Anisometry of the EPR droplets and droplet shape relaxation were perceived, both interfering the course of coalescence. Enhanced elasticity of examined blends at low frequencies and positive deviation of the complex viscosity from the linear mixing rules was observed.