Optically-transparent oxide fibre-reinforced glass matrix composites

  1. 1.
    0355562 - ÚFM 2011 RIV NL eng J - Článek v odborném periodiku
    Desimone, D. - Dlouhý, Ivo - Lee, W. E. - Koch, D. - Horvath, J. - Boccaccini, A. R.
    Optically-transparent oxide fibre-reinforced glass matrix composites.
    Journal of Non-Crystalline Solids. Roč. 356, 44-49 (2010), s. 2591-2597. ISSN 0022-3093. E-ISSN 1873-4812
    Grant CEP: GA ČR GA101/09/1821
    Výzkumný záměr: CEZ:AV0Z20410507
    Klíčová slova: fracture toughness * glas matrix composites * light transmittance
    Kód oboru RIV: JH - Keramika, žáruvzdorné materiály a skla
    Impakt faktor: 1.483, rok: 2010

    Development of ‘optomechanical composites’, based on glass matrices reinforced with continuous oxide fibre bundles (Nextel™) or filaments (sapphire) is described. The fibres were arranged unidirectionally between soda-lime silicate or borosilicate glass slides, and heat-treated to achieve densification by viscous flow of the glass matrix between the fibres. Small decreases in light transmittance (up to approximately 20%) upon introduction of fibres was indicated. Fibre pull-out and crack deflection were identified at fibre/matrix interfaces, and a crack bridging effect was observed, with fibres holding the glass pieces together, thus preventing catastrophic failure. A relatively low fibre/matrix interfacial sliding resistance was measured by the fibre push-in test, although flexural strength measurements indicated the need to improve interfacial bonding.
    Trvalý link: http://hdl.handle.net/11104/0194306

     
     