SANS Investigation of Y ' Precipitate Morphology Evolution in Creep Exposed Single Crystal Ni base Superalloy

0347276 - ÚJF 2011 RIV CH eng C - Konferenční příspěvek (zahraniční konf.)
Zrnik, J. - Strunz, Pavel - Maldini, M. - Davydov, Vadim
SANS Investigation of Y ' Precipitate Morphology Evolution in Creep Exposed Single Crystal Ni base Superalloy.
ADVANCED MATERIALS FORUM V, PT 1 AND 2. CH-8717 STAFA-ZURICH: TRANS TECH PUBLICATIONS LTD, LAUBLSRUTISTR 24, 2010 - (Rosa, L.; Margarido, F.), s. 1475-1482. ISSN 0255-5476.
[5th International Materials Symposium/14th Conference of the Sociedade-Portuguesa-de-Materiais. Lisbon (PT), 05.04.2009-08.04.2009]
Výzkumný záměr: CEZ:AV0Z10480505
Klíčová slova: Nickel base superalloys * Single crystal * Creep
Kód oboru RIV: BG - Jaderná, atomová a mol. fyzika, urychlovače

The creep degraded nickel base single crystal superalloy CMSX-4 of two axial orientations [001] and [111] was investigated with aim to assess the structure degradation. Constant load creep tests were conducted in the stress/temperature ranges of 250-780 MPa/750 - 50 degrees C resulting in rupture time variation from 50 to 4000 hours. A combination of scanning electron microscopy (SEM) and non-destructive small-angle neutron scattering method (SANS) was used to. investigate the directional coarsening (rafting) of the gamma prime (gamma') precipitates in relation to the stress and temperature applied as well as to the initial crystallographic orientation of the specimens. The SANS results are discussed in terms of the correlation with the raft development, the axial orientation of specimen, the creep parameters and the mechanical properties.