Study of microstructure in Ag-x(As0.33Se0.67)(100-x) chalcogenide glasses.
[Studium mikrostruktury v chalkogenidových sklech Agx(As0.33Se0.67)100-x.]
Journal of Non-Crystalline Solids. Roč. 355, 37-42 (2009), s. 2054-2058. ISSN 0022-3093. E-ISSN 1873-4812
Výzkumný záměr: CEZ:AV0Z40500505
Klíčová slova: conductivity
Kód oboru RIV: CA - Anorganická chemie
Impakt faktor: 1.252, rok: 2009

Glasses with general formula Ag(As33Se67)100-x were studied by means of MDSC, conductivity and permittivity measurements and atomic force acoustic microscopy (AFAM). The proportional amount of the ion-conductive Ag rich phase indcreased with the Ag content. A rapid increase (almost 4 orders of magnitude) in the conductivity was observed in the Ag concentration range 4-8 at%, which could be associated with the interconnection of this ion-conductive phase. The transition from an electronic (hole) conductivity (at low Ag concentration) to a mixed ionic-electronic (hole) conductivity at higher Ag concentration was studied by permittivity measurements.

Skla s obecným složením Agx(As33Se67)100-x byly studovány pomocí MDSC, vodivosti, permitivity a mikroskopií atomových akustických sil (AFAM). Poměrní množství iontově vodivé stříbrem bohaté fáze stoupá s obsahem stříbra. Prudký růst vodivosti (téměř o čtyří řády) byl pozorován v koncentračním rozmezí stříbra 4-8%, což může být spojeno s propojením této iontově vodivé fáze. Přechod od elektronové (děrové) vodivosti (při nízkých koncentracích stříbra) ke směsné intově-elektronové (děrové) vodivosti při vyšších koncentracích Ag byl studován pomocí měření permitivity.