Correlating Microstrain and Activated Slip Systems with Mechanical Properties within Rotary Swaged WNiCo Pseudoalloy
- 1.
SYSNO ASEP 0523499 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Correlating Microstrain and Activated Slip Systems with Mechanical Properties within Rotary Swaged WNiCo Pseudoalloy Tvůrce(i) Strunz, Pavel (UJF-V) RID, ORCID, SAI
Kunčická, L. (CZ)
Beran, Přemysl (UJF-V) RID, ORCID, SAI
Kocich, R. (CZ)
Hervoches, Charles (UJF-V) RID, ORCID, SAICelkový počet autorů 5 Číslo článku 208 Zdroj.dok. Materials. - : MDPI
Roč. 13, č. 1 (2020)Poč.str. 15 s. Forma vydání Online - E Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova tungsten ; rotary swaging ; neutron diffraction ; dislocations ; microstrain Vědní obor RIV BM - Fyzika pevných látek a magnetismus Obor OECD Condensed matter physics (including formerly solid state physics, supercond.) CEP GA19-15479S GA ČR - Grantová agentura ČR LM2015056 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy EF16_013/0001812 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Výzkumná infrastruktura Reactors LVR-15 and LR-0 II - 90120 - Centrum výzkumu Řež s.r.o. Způsob publikování Open access Institucionální podpora UJF-V - RVO:61389005 UT WOS 000515499300208 EID SCOPUS 85079815494 DOI 10.3390/ma13010208 Anotace Due to their superb mechanical properties and high specific mass, tungsten heavy alloys are used in demanding applications, such as kinetic penetrators, gyroscope rotors, or radiation shielding. However, their structure, consisting of hard tungsten particles embedded in a soft matrix, makes the deformation processing a challenging task. This study focused on the characterization of deformation behavior during thermomechanical processing of a WNiCo tungsten heavy alloy (THA) via the method of rotary swaging at various temperatures. Emphasis is given to microstrain development and determination of the activated slip systems and dislocation density via neutron diffraction. The analyses showed that the grains of the NiCo2W matrix refined significantly after the deformation treatments. The microstrain was higher in the cold swaged sample (44.2 x 10(-4)). Both the samples swaged at 20 degrees C and 900 degrees C exhibited the activation of edge dislocations with 111 {110} or 110 {111} slip systems, and/or screw dislocations with 110 slip system in the NiCo2W matrix. Dislocation densities were determined and the results were correlated with the final mechanical properties of the swaged bars. Pracoviště Ústav jaderné fyziky Kontakt Markéta Sommerová, sommerova@ujf.cas.cz, Tel.: 266 173 228 Rok sběru 2021 Elektronická adresa https://doi.org/10.3390/ma13010208
Počet záznamů: 1