ODS EUROFER Steel Strengthened by Y-(Ce, Hf, La,\nSc, and Zr) Complex Oxides
- 1.
SYSNO ASEP 0510160 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název ODS EUROFER Steel Strengthened by Y-(Ce, Hf, La,
Sc, and Zr) Complex OxidesTvůrce(i) Husák, Roman (UFM-A)
Hadraba, Hynek (UFM-A) RID, ORCID
Chlup, Zdeněk (UFM-A) RID, ORCID
Heczko, Milan (UFM-A) ORCID
Kruml, Tomáš (UFM-A) RID, ORCID
Puchý, V. (SK)Celkový počet autorů 6 Číslo článku 1148 Zdroj.dok. Metals. - : MDPI
Roč. 9, č. 11 (2019)Poč.str. 14 s. Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova oxide dispersion-strengthened steel ; low-activation steel ; mechanical alloying ; spark plasma sintering ; complex oxide Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering CEP GA17-23964S GA ČR - Grantová agentura ČR Způsob publikování Open access Institucionální podpora UFM-A - RVO:68081723 UT WOS 000504411600016 EID SCOPUS 85076803877 DOI 10.3390/met9111148 Anotace Oxide dispersion-strengthened (ODS) materials contain homogeneous dispersions of
temperature-stable nano-oxides serving as obstacles for dislocations and further pinning of grain
boundaries. The strategy for dispersion strengthening based on complex oxides (Y-Hf, -Zr, -Ce, -La)
was developed in order to refine oxide dispersion to enhance the dispersion strengthening e ect.
In this work, the strengthening of EUROFER steel by complex oxides based on Y and elements of
the IIIB group (lanthanum, scandium) and IVB group (cerium, hafnium, zirconium) was explored.
Interparticle spacing as a dispersoid characteristic appeared to be an important factor in controlling the
dispersion strengthening contribution to the yield strength of ODS EUROFER steels. The dispersoid
size and average grain size of ODS EUROFER steel were altered in the ranges of 5–13 nm and
0.6–1.7 m, respectively. Using this strategy, the yield strength of the prepared alloys varied between
550 MPa and 950 MPa depending on the doping elementPracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2020 Elektronická adresa https://www.mdpi.com/2075-4701/9/11/1148/htm