Mechanical behaviour of ferritic ODS steels - Temperature dependancy and history

  1. 1.
    SYSNO ASEP0379831
    Druh ASEPJ - Článek v odborném periodiku
    Zařazení RIVJ - Článek v odborném periodiku
    Poddruh JČlánek ve WOS
    NázevMechanical behaviour of ferritic ODS steels - Temperature dependancy and history
    Tvůrce(i) Fournier, B. (FR)
    Steckmeyer, A. (FR)
    Rouffié, A.-L. (FR)
    Malaplate, J. (FR)
    Garnier, J. (FR)
    Ratti, M. (FR)
    Wident, P. (FR)
    Ziolek, L. (FR)
    Tournie, I. (FR)
    Rabeau, V. (FR)
    Gentzbittel, J.M. (FR)
    Kruml, Tomáš (UFM-A) RID, ORCID
    Kuběna, Ivo (UFM-A) RID, ORCID
    Celkový počet autorů13
    Zdroj.dok.Journal of Nuclear Materials. - : Elsevier - ISSN 0022-3115
    Roč. 430, 1-3 (2012), s. 142-149
    Poč.str.8 s.
    Jazyk dok.eng - angličtina
    Země vyd.NL - Nizozemsko
    Klíč. slovaODS steels ; fatigue ; fracture mechanics
    Vědní obor RIVJL - Únava materiálu a lomová mechanika
    Institucionální podporaUFM-A - RVO:68081723
    UT WOS000310940700021
    DOI https://doi.org/10.1016/j.jnucmat.2012.05.048
    AnotaceFerritic 14%Cr and 18%Cr ODS steels produced at CEA in round bars or plates were tested mechanically. The present paper reports results obtained in tension, impact, fatigue, creep and toughness tests. These tests were carried out at various temperatures and in different directions. These materials show a pronounced anisotropy at all tested temperatures. No matter the loading, the transversal direction is always found to be far less resistant than the longitudinal one. This anisotropy is mainly observed in terms of damage mechanisms, with intergranular fracture preferentially occurring along the extrusion direction. This intergranular fracture mode leads to very low and anisotropic toughness values and to the absence of tertiairy creep stage, pointing out the unstable nature of fracture, even at high temperature. The unrealistically high values of the Norton exponent measured in creep suggests the existence of a threshold stress, which is consistent with the mainly kinematic nature of the stress as revealed by fatigue tests.
    PracovištěÚstav fyziky materiálu
    KontaktYvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485
    Rok sběru2013
Počet záznamů: 1  

  Tyto stránky využívají soubory cookies, které usnadňují jejich prohlížení. Další informace o tom jak používáme cookies.