Corrosion behavior of titanium silicide surface with hydrogen peroxide: formation of sub-μm TiOx- based spheres, nanocomposite TiOx/SiOx phases, and mesoporous TiOx/SiOx network.
- 1.0525519 - ÚACH 2021 RIV NL eng J - Článek v odborném periodiku
Jandová, V. - Fajgar, R. - Kupčík, Jaroslav - Pola, J. - Soukup, K. - Mikysek, P. - Křenek, T. - Kovářík, T. - Stich, T. - Docheva, D.
Corrosion behavior of titanium silicide surface with hydrogen peroxide: formation of sub-μm TiOx- based spheres, nanocomposite TiOx/SiOx phases, and mesoporous TiOx/SiOx network.
Applied Surface Science. Roč. 529, NOV (2020), č. článku 147133. ISSN 0169-4332. E-ISSN 1873-5584
Institucionální podpora: RVO:61388980
Klíčová slova: titanium silicide SiOx microphases * hydrogen peroxide * SiOx microphases
Obor OECD: Inorganic and nuclear chemistry
Impakt faktor: 6.707, rok: 2020
Způsob publikování: Open access s časovým embargem
So far unexplored corrosion of titanium silicide (Ti5Si3) surface with acidified hydrogen peroxide is of interest due to its potential use in improving osseointegration of titanium implants coated by titanium silicides. Detailed examination of corrosion products by FTIR, Raman and XP spectroscopy, electron microscopy, XRD, BET and light scattering techniques allows recognition of hydrated nanocomposite TiOx/SiOx (x <= 2) phases composed of segregated amorphous SiOx species and TiOx-based networks containing Ti-O-Si and -O-O-bonds. The appearance of the TiOx networks depends on the extent of peroxidation. A less progressed peroxidation yields sub mu m-sized TiOx-based spheres which upon annealing develop anatase nanograins withstanding 800 degrees C. A more progressed peroxidation produces larger mesoporous TiOx-based bodies which disintegrate upon sonication into micrometer-sized entities. The proposed mechanism of surface corrosion is based on the complementary use of analytical techniques. The one-step production of bioactive (hydrated TiOx and SiOx) species deserves to be explored in osseointegration studies of slightly corroded Ti5Si3-coated titanium implants.
Trvalý link: http://hdl.handle.net/11104/0310101