Mechanisms of high temperature damage in elastoplastic cyclic loading of nickel superalloys and TiAl intermetallics
- 1.
SYSNO ASEP 0435829 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Mechanisms of high temperature damage in elastoplastic cyclic loading of nickel superalloys and TiAl intermetallics Tvůrce(i) Polák, Jaroslav (UFM-A) RID, ORCID
Obrtlík, Karel (UFM-A) RID, ORCID
Petrenec, Martin (UFM-A)
Man, Jiří (UFM-A) RID, ORCID
Kruml, Tomáš (UFM-A) RID, ORCIDCelkový počet autorů 5 Zdroj.dok. 6TH INTERNATIONAL CONFERENCE ON CREEP, FATIGUE AND CREEP-FATIGUE INTERACTION. - Amsterdam : Elsevier, 2013 / Chetal CS. ; Jayakumar T. ; Sandhya R. ; Laha K. ; Mathew MD. - ISSN 1877-7058 Rozsah stran s. 114-122 Poč.str. 9 s. Forma vydání Tištěná - P Akce International Conference on Creep, Fatigue and Creep-Fatigue Interaction /6./ Datum konání 22.01.2012-25.01.2012 Místo konání Mamallapuram Země IN - Indie Typ akce WRD Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova fatigue damage ; crack initiation ; high temperature ; nickel superalloy ; TiAl intermetallics Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP GAP107/11/0704 GA ČR - Grantová agentura ČR GAP107/11/2065 GA ČR - Grantová agentura ČR GAP204/11/1453 GA ČR - Grantová agentura ČR Institucionální podpora UFM-A - RVO:68081723 UT WOS 000335733500019 DOI 10.1016/j.proeng.2013.03.229 Anotace The mechanisms of the fatigue damage in nickel superalloys and TiAl intermetallics used for the design of components working at elevated temperatures are studied. The characteristic surface relief and the accompanying internal dislocation structures of these materials subjected to strain controlled cycling are documented using high resolution SEM, AFM and TEM. Typical structures corresponding to cyclic strain localization are shown in each class of materials and they are discussed in relation to the characteristic internal structure of a particular material and the types of dislocations participating in cyclic plastic deformation. The relation between surface persistent slip markings (extrusions and intrusions) and persistent slip bands in the interior of the material is presented. The mechanisms leading to fatigue crack initiation and early crystallographic crack growth are discussed. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2015
Počet záznamů: 1