Fatigue crack initiation and growth in 316L steel in torsional cyclic loading

0494057 - ÚFM 2019 RIV CZ eng C - Konferenční příspěvek (zahraniční konf.)
Karol, Michal - Chlupová, Alice - Mazánová, Veronika - Kruml, Tomáš
Fatigue crack initiation and growth in 316L steel in torsional cyclic loading.
Engineering Mechanics 2017 : 23rd international conference : May 15-18, 2017, Svratka, Czech Republic : book of full texts. Brno: University of Technology, Institute of Solid Mechanics, Mechatronics and Biomechanics, 2017 - (Fuis, V.), s. 434-437. ISBN 978-80-214-5497-2.
[Engineering Mechanics 2017 - International Conference /23./. Svratka (CZ), 15.05.2017-18.05.2017]
Grant CEP: GA MŠMT LM2015069; GA ČR GA15-08826S
Institucionální podpora: RVO:68081723
Klíčová slova: 316L austenitic steel * fatigue crack initiation * Crack growth * Torsional loading * Crack path
Obor OECD: Materials engineering

Fatigue crack initiation and growth study in 316L austenitic stainless steel was made in cyclic
torsion. The experiments on hollow cylindrical specimens were performed at room temperature using fully reversed shear strain controlled cycles. The specimens used were polished mechanically and electrolytically to enable surface damage and crack propagation observation using optical light microscope, SEM. It was found that high density of extrusions and intrusions are formed on the specimen surface due to cyclic loading. TEM observations revealed that dislocation arrangement in well-known ladder-like structure is responsible for the localization of cyclic plastic deformation and for the origin of surface roughness in which the fatigue crack nucleate. The path of fatigue cracks leading to failure was observed, too. The crack path
was found to be dependent upon the applied shear strain amplitude.
Trvalý link: http://hdl.handle.net/11104/0289464