Comparison of low cycle fatigue of ductile cast irons with different matrix alloyed with nickel

0355181 - ÚFM 2011 RIV NL eng J - Článek v odborném periodiku
Petrenec, Martin - Tesařová, H. - Beran, Přemysl - Šmíd, Miroslav - Roupcová, Pavla
Comparison of low cycle fatigue of ductile cast irons with different matrix alloyed with nickel.
Procedia Engineering. Roč. 2, č. 1 (2010), s. 2307-2316. E-ISSN 1877-7058.
[Fatigue 2010. Praha, 06.06.2010-11.06.2010]
Grant CEP: GA ČR GAP108/10/2371
Výzkumný záměr: CEZ:AV0Z20410507; CEZ:AV0Z10480505
Klíčová slova: Low cycle fatigue * ferritic ductile cast iron * ADI * nickel alloying * neutron diffraction
Kód oboru RIV: JL - Únava materiálu a lomová mechanika

Total strain controlled tests have been performed on cylindrical specimens of austempered ductile cast iron (ADI) and ductile cast iron with the ferritic matrix, both alloyed with 2.75% Ni, with the aim to compare cyclic plasticity and the fatigue life at temperatures 23 °C and–45 °C.In ADI the measurement of retained austenite by neutron diffraction before and after fatigue tests is used to discuss the cyclic stress-strain response. Cyclic hardening/softening curves, cyclic stress-strain curves and fatigue life curves were obtained for both temperatures and materials. Cyclic stress-strain curve obtained at–45 °C is shifted to higher stress amplitudes relative to room temperature curve. The Manson-Coffin curves are identical for both materials and temperatures while the Basquin curve is shifted to longer fatigue life for ADI. The surface relief developed during fatigue was studied using SEM. Fatigue cracks initiated preferably from persistent slip markings at the interface of graphite nodule.