Degradation Processes of Medieval and Renaissance Glazed Ceramics
- 1.0567751 - ÚSMH 2024 RIV CH eng J - Článek v odborném periodiku
Kolářová, M. - Kloužková, A. - Kohoutková, M. - Kloužek, Jaroslav - Dvořáková, P.
Degradation Processes of Medieval and Renaissance Glazed Ceramics.
Materials. Roč. 16, č. 1 (2023), č. článku 375. ISSN 1996-1944. E-ISSN 1996-1944
Institucionální podpora: RVO:67985891
Klíčová slova: archaeological lead-glazed ceramics * archaeometric characterisation * degradation * glaze fit
Obor OECD: Ceramics
Impakt faktor: 3.1, rok: 2023
Způsob publikování: Open access
https://doi.org/10.3390/ma16010375
Corrosion effects in deposit environments (soil, waste pit, etc.), together with the glaze adherence and fit, could cause severe deterioration accompanied by different types of defects or growth of corrosion products. The aim of this work was to identify the source of surface degradation of the lead-glazed ceramics sets from the Prague area from the Romanesque to the Renaissance period. A combination of X-ray fluorescence (XRF), X-ray diffraction (XRD), optical microscopy (OM), scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM/EDS), and simultaneous thermal analysis (STA) techniques along with stress state calculations was used to study the defects. Based on the interpretation of the possible sources of the observed defects, four types of degradation effects were schematically expressed for the archaeological samples. It was shown that the glazes were already appropriately chosen during the production of the Romanesque tiles and that their degradation occurred only due to long-term exposure to unsuitable environmental conditions.