Study of water uptake in poly(ether ether ketone) irradiated by MeV O+ and Au+ ions
- 1.0523922 - ÚJF 2021 RIV GB eng J - Článek v odborném periodiku
Hnatowicz, Vladimír - Vacík, Jiří - Horák, Pavel
Study of water uptake in poly(ether ether ketone) irradiated by MeV O+ and Au+ ions.
Radiation Effects and Defects in Solids. Roč. 175, 3-4 (2020), s. 318-324. ISSN 1042-0150. E-ISSN 1029-4953
Grant CEP: GA ČR GA18-07619S; GA MŠMT LM2015056
Institucionální podpora: RVO:61389005
Klíčová slova: Poly(ether ether ketone) * ion irradiation * LiCl doping * neutron depth profiling * diffusion
Obor OECD: Materials engineering
Impakt faktor: 1.141, rok: 2020
Způsob publikování: Omezený přístup
https://doi.org/10.1080/10420150.2019.1701463
Poly(ether ether ketone) (PEEK) was irradiated with 4 MeV O+ and 5 and 10 MeV Au+ ions to the fluences from 10(12) to 10(14 )cm(-2) and then treated in 5 M/l water solution of LiCl for one month at room temperature. After drying and removal of LiCl surface contamination, the depth distribution of LiCl embeded in PEEK was measured by the neutron depth profilig method (NDP) sensitive to Li-6 isotope. Embeded LiCl is believed to map distribution of water diffusing into PEEK interior. The results show that the PEEK irradiated to the fluences above 1.10(13)cm(-2) is prone to water penetration to the depths of few microns. On the pristine PEEK and that irradiated to lower ion fluences only a surface Li contamination is observed.