Response of fusion plasma-facing materials to nanosecond pulses of extreme ultraviolet radiation

0499585 - ÚFP 2019 RIV US eng J - Článek v odborném periodiku
Štraus, Jaroslav - Koláček, Karel - Schmidt, Jiří - Frolov, Oleksandr - Vilémová, Monika - Matějíček, Jiří - Jäger, A. - Juha, Libor - Toufarová, M. - Choukorov, A. - Kasuya, K.
Response of fusion plasma-facing materials to nanosecond pulses of extreme ultraviolet radiation.
Laser and Particle Beams. Roč. 36, č. 3 (2018), s. 293-307. ISSN 0263-0346. E-ISSN 1469-803X
Grant CEP: GA ČR(CZ) GA14-29772S; GA ČR(CZ) GA14-12837S; GA MŠMT LG15013; GA MŠMT LM2015087; GA MŠMT LTT17015
Institucionální podpora: RVO:61389021
Klíčová slova: Interaction of XUV with matter * plasma-facing materials * XUV radiation resistance
Obor OECD: Fluids and plasma physics (including surface physics)
Impakt faktor: 1.194, rok: 2018
https://www.cambridge.org/core/services/aop-cambridge-core/content/view/94EC0B3668AFF31234394BA12636C21C/S0263034618000332a.pdf/response_of_fusion_plasmafacing_materials_to_nanosecond_pulses_of_extreme_ultraviolet_radiation.pdf

The experimental study of damage to tungsten (W), molybdenum (Mo), and silicon carbide (SiC) surfaces induced by focused extreme ultraviolet laser radiation (lambda similar to 47 nm/similar to 1.5 ns/21-40 mu J) is presented. It was found that W and Mo behaved similarly: during the first shot, the damaged area is covered by melted and re-solidified material, in which circular holes appear residua of just opened pores/bubbles, from which pressurized gas/vapors escaped. Next cracks and ruptures appear and the W has a tendency to delaminate its surface layer. Contrary, single-crystalline SiC has negligible porosity and sublimates, therefore, no escape of 'pressurized' gas and no accompanying effects take place. Moreover, SiC at sublimating temperature decomposes to elements, therefore, the smooth crater morphology can be related to local laser energy density above ablation threshold. When more shots are accumulated, in all three investigated materials, the crater depth increases non-linearly with number of these shots. The surface morphology was investigated by an atomic force microscope, the surface structure was imaged by a scanning electron microscope (SEM), and the structure below the surface was visualized by SEM directed into a trench that is milled by focused ion beam. Additionally, structural changes in SiC were revealed by Raman spectroscopy.