Fatigue crack propagation in UFG Ti grade 4 processed by severe plastic deformation

  1. 1.
    0471662 - UFM-A 2018 RIV GB eng J - Článek v odborném periodiku
    Fintová, Stanislava - Arzaghi, M. - Kuběna, Ivo - Kunz, Ludvík - Sarrazin-Baudoux, C.
    Fatigue crack propagation in UFG Ti grade 4 processed by severe plastic deformation.
    International Journal of Fatigue. Roč. 98, MAY (2017), s. 187-194. ISSN 0142-1123
    Grant CEP: GA MŠk(CZ) LQ1601; GA MŠk LM2015069
    Institucionální podpora: RVO:68081723
    Klíčová slova: Titanium * Fatigue * Crack growth * Crack closure * Equal channel angular processing
    Kód oboru RIV: JL - Únava materiálu a lomová mechanika
    Obor OECD: Audio engineering, reliability analysis
    Impakt faktor: 3.132, rok: 2017
    http://www.sciencedirect.com/science/article/pii/S014211231730035X

    Fatigue crack growth was investigated in commercially pure Ti grade 4 processed by severe plastic deformation. The ultrafine-grained structure was prepared by means of equal channel angular pressing technique followed by cold drawing. The growth of fatigue cracks was investigated also in the as-received coarse-grained state of material for comparison.
    The fatigue crack growth rate in the ultrafine-grained material was found to be higher and the threshold stress intensity range delta Kth for crack growth lower than in the coarse-grained Ti, 2.5 and 4.7 MPa m1/2, respectively. A combination of transcrystaline and intercrystaline crack growth was typical for all crack growth rates in the coarse-grained material. Contrary to the combined fracture mechanism in coarse-grained Ti only transcrystalline crack growth was a characteristic feature of crack propagation in the ultrafine-grained material.
    It has been found that the experimentally and theoretically determined values of closure are in reasonable agreement. Crack closure calculated according to the Newman model taking into account only plasticity induced closure was in the range from 67% to 69% of Kmax for as-received and 70% for UFG state of material. Crack closure determined experimentally was 67% of Kmax for as-received and 67% for UFG CP Ti grade 4.
    Investigation of fracture surfaces did not bring any evident signs of the effects of fracture surface morphology resulting in roughness induced closure or oxide induced closure under testing conditions used. This indicates that plasticity induced closure seems to be a dominant closure mechanism in both states of the investigated Ti grade 4.