Synthesis of Magnetic Ultrafine Particles from a Ternary Gaseous Mixture Involving Cobalt Tricarbonyl Nitrosyl

  1. 1.
    0440069 - ÚACH 2015 RIV JP eng J - Článek v odborném periodiku
    Morita, H. - Sakano, H. - Murafa, Nataliya - Šubrt, Jan
    Synthesis of Magnetic Ultrafine Particles from a Ternary Gaseous Mixture Involving Cobalt Tricarbonyl Nitrosyl.
    Journal of Photopolymer Science and Technology. Roč. 27, č. 46 (2014), s. 477-483. ISSN 0914-9244. E-ISSN 1349-6336
    Institucionální podpora: RVO:61388980
    Klíčová slova: gas phase photochemical reaction * magnetic ultrafine particle * cobalt tricarbonyl nitrosyl * tetraethylgermane * propenyltrimethylsilane
    Kód oboru RIV: CA - Anorganická chemie
    Impakt faktor: 1.055, rok: 2014

    From a ternary gaseous mixture of cobalt tricarbonyl nitrosyl (Co(CO)(3)NO), tetraethylgermane (TEG), and propenyltrimethylsilane (allyltrimethylsilane) (ATMeSi), magnetic ultrafine particles were produced under irradiation with intense Nd:YAG laser light. From FT-IR spectra, chemical structure of the ultrafine particles was investigated. The spectrum of the magnetic particles was essentially the same to the one of the ultrafine particles produced from a binary gaseous mixture of Co(CO)(3)NO and ATMeSi, suggesting strongly that TEG molecules did not contribute significantly to particle formation process. On the other hand, in the gaseous phase, depletion rate of TEG molecules was accelerated by 800 times due to the presence of Co(CO)(3)NO molecules, showing that TEG molecules interacted efficiently with Co(CO)(3)NO molecules to produce some volatile chemical species in the gas phase under laser light irradiation. Magnetization of the ultrafine particles was measured using a SQUID magnetometer. Magnetic susceptibility of the ultrafine particles was evaluated to be similar to 1 x 10(-2) emu/g, suggesting that the deposited ultrafine particles were mainly composed of ferromagnetic species. The morphology of the coagulated particles was studied by taking HRTEM images. The ultrafine particles were composed of several kinds of particles which involved both the polycrystalline phase and amorphous phase. Crystalline phase was mainly composed of Co atoms, and may be responsible for ferromagnetic properties of the particles.