Influence of applied tensile stress on the hysteresis curve and magnetic domain structure of grain-oriented Fe–3%Si steel

  1. 1.
    0430380 - FZÚ 2015 RIV GB eng J - Článek v odborném periodiku
    Perevertov, Oleksiy - Schäfer, R.
    Influence of applied tensile stress on the hysteresis curve and magnetic domain structure of grain-oriented Fe–3%Si steel.
    Journal of Physics D-Applied Physics. Roč. 47, č. 18 (2014), s. 1-10. ISSN 0022-3727
    Grant CEP: GA ČR(CZ) GAP107/11/0391
    Grant ostatní:AVČR(CZ) M100100906
    Institucionální podpora: RVO:68378271
    Klíčová slova: magnetic domains * magnetization process * magnetoelasticity * hysteresis loops * tension * silicon steel * Kerr microscopy
    Kód oboru RIV: BM - Fyzika pevných látek a magnetismus
    Impakt faktor: 2.721, rok: 2014

    The influence of applied tensile stress on the hysteresis curve and domain structure in conventional (1 1 0)[0 0 1] Fe–3%Si steel, cut parallel to the rolling direction, is studied on samples with different grain sizes. Quasistatic hysteresis loops under tensile stresses up to 70MPa were measured. The magnetic domains and magnetization processes were observed by longitudinal Kerr microscopy at different levels of stress. It is shown that for stresses exceeding 5–10MPa the bulk hysteresis loop can be described with good accuracy by the action of an effective field, which is the product of a function of stress and a function of magnetization. The function of stress is approximately linear with a slope of one. Except for the sample with the smallest grains, the function of magnetization is linear in the magnetization range ±1.2–1.5 T, i.e. it has a typical demagnetizing field shape.