Thermomagnetic Analysis of Nanocrystalline Nd4.5Fe77B18.5 Alloy

0339958 - ÚFM 2010 RIV JP eng J - Článek v odborném periodiku
Talijan, N. - Ćosović, V. - Stajić-Trošić, J. - Grujić, A. - Žák, Tomáš - Lee, Z. - Radmilović, V.
Thermomagnetic Analysis of Nanocrystalline Nd4.5Fe77B18.5 Alloy.
Materials Transactions. Roč. 50, č. 9 (2009), s. 2302-2307. ISSN 1345-9678. E-ISSN 1347-5320
Grant CEP: GA MŠMT 1M0512
Výzkumný záměr: CEZ:AV0Z20410507
Klíčová slova: low-neodymium neodymium-iron-boron alloy * thermomagnetic measurements * X-ray diffraction * magnetic properties
Kód oboru RIV: BM - Fyzika pevných látek a magnetismus
Impakt faktor: 0.795, rok: 2009

Changes in the phase composition and crystallite size of a rapid quenched Nd4.5Fe77B18.5 alloy, caused by thermomagnetic measurements (TM) have been studied using XRD methods of phase analysis. crystallite size and lattice microstrain determination. Structural changes in regard to optimal magnetic state were additionally analyzed by TEM. Magnetic properties in optimal magnetic state and after TM were observed using room temperature SQUID measurements. The obtained experimental results suggest the Fe3B/Nd2Fe14B and partly alpha-Fe nanocomposite structure of the alloy in the optimized magnetic state. with mean crystallite size (< 30nm). After TM. an increased amount of alpha-Fe phase, presence of different oxide and Fe-B phases as well as growth of crystallites are found to be the main reasons for the observed quality loss of hard magnetic properties.