Constraint Effect on Environmentally Assisted Cracking of the Austenite Steel 08Kh18N10T in the Concentrated Solutions at 270 degrees of Celsius

  1. 1.
    0210180 - UTAM-F 20000086 RIV SIGLE ES eng C - Konferenční příspěvek (zahraniční konf.)
    Brožová, A. - Šplíchal, K. - Fiala, Zdeněk
    Constraint Effect on Environmentally Assisted Cracking of the Austenite Steel 08Kh18N10T in the Concentrated Solutions at 270 degrees of Celsius.
    13th European Conference on Fracture. San Sebastian: Elsevier, 2000, s. 10-16.
    [European Conference on Fracture /13./. San Sebastian (ES), 06.09.2000-09.09.2000]
    Grant CEP: GA AV ČR KSK1010601
    Klíčová slova: environmentally assisted cracking.
    Kód oboru RIV: JK - Koroze a povrchové úpravy materiálů

    Experimental results of accelerated environmentally assisted cracking tests demonstrate that constraint significantly affects the crack growth. Using FEM crack tip strain rates were then evaluated at point of crack initiation.