Effect of T-stress on dislocation emission in iron

  1. 1.
    0103497 - UT-L 20040003 RIV NL eng J - Článek v odborném periodiku
    Beltz, G. E. - Machová, Anna
    Effect of T-stress on dislocation emission in iron.
    [Vliv T-napětí na emisi dislokací v železe.]
    Scripta Materialia. Roč. 50, č. 50 (2004), s. 483-487. ISSN 1359-6462. E-ISSN 1872-8456
    Grant CEP: GA AV ČR IAA2076201; GA MŠk ME 504
    Grant ostatní: NSF(US) CMS0000142
    Výzkumný záměr: CEZ:AV0Z2076919
    Klíčová slova: dislocation * emission * iron
    Kód oboru RIV: JG - Hutnictví, kovové materiály
    Impakt faktor: 2.112, rok: 2004

    Continuum predictions for dislocation emission from a crack tip loaded under mode I, biaxial conditions, are compared with atomistic results for bcc iron. The simulations validate the continuum prediction that, as the T-stress increases, so does the threshold for dislocation nucleation; hence, the propensity for brittle response increases.

    Predikce kontinua o emisi dislokací od kořene trhliny, zatíženého v tahovém módu I a biaxiálně, jsou porovnány s atomárními výsledky pro alfa železo. Atomární simulace potvrzují predikci kontinua, že se vzrůstem T-napětí se zvyšuje práh pro nukleaci dislokací a tudíž pravděpodobnost křehkého lomu vzrůstá.