Tensile/compressive behaviour of non-lyered tetragonal Ni.sub.52.8./sub.Mn.sub.25.7./sub.Ga.sub.21.5./sub. alloy
- 1.0102492 - FZU-D 20040543 RIV NL eng J - Článek v odborném periodiku
Söderberg, O. - Straka, L. - Novák, Václav - Heczko, O. - Hannula, S.-P. - Lindroos, V. K.
Tensile/compressive behaviour of non-lyered tetragonal Ni52.8Mn25.7Ga21.5 alloy.
[Tahové/tlakové chování nevrstevné slitiny Ni52.8Mn25.7Ga21.5]
Materials Science and Engineering A Structural Materials Properties Microstructure and Processing. Roč. 386, - (2004), s. 27-33. ISSN 0921-5093. E-ISSN 1873-4936
Výzkumný záměr: CEZ:AV0Z1010914
Klíčová slova: Ni-Mn-Ga alloys * tensile testing * twinning
Kód oboru RIV: BM - Fyzika pevných látek a magnetismus
Impakt faktor: 1.445, rok: 2004
The stress-strain behaviour of the alloy NiMnGa with the non-modulated tetragonal martensite crystal structure was studied below Ms temperature. At ambient temperature the stress plateau of the detwinning showed a total strain of 21-22% with 1S-20MPa stress. The tension-compression cycling decreased the stress plateau to 10-12 MPa, while the increasing testing temperature lead to a value of 6.7 MPa close to the reverse transformation temperature
Deformační chování ve slitině NiMnGa s nemodulovanou tetragonální martensitickou krystalovou strukturou bylo studováno pod Ms teplotou. Při pokojové teplotě napěťové plato pro detwinning vykazuje celkovou deformaci 21-22% při napětí 15-20 MPa. Cyklování tah-tlak snižuje napětí plata na 10-12 MPa, zatímco rostoucí teplota testu vede k hodnotě 6-7 MPa v blízkosti teploty zpětné transformace