Silicalite-1 - Polyimide Composites.
[Kompozity na bázi silikalit-1- polyimidy.]
Proceedings. CHISA 2004. Praha, 2004, P3.182.
[International Congress of Chemical and Process Engineering CHISA 2004 /16./. Praha (CZ), 22.08.2004-26.08.2004]
Grant CEP: GA ČR GA104/03/0680
Výzkumný záměr: CEZ:AV0Z4040901
Klíčová slova: polyimide * silicalite-1 * composites
Kód oboru RIV: CF - Fyzikální chemie a teoretická chemie

Two methods of adhesion improvement between the polyimide matrix and zeolite (silicalite-1) were examined. Firstly, there were prepared polyimide precursors (polyamic acids) with controlled molecular weight terminated with 3-aminopropyltriethoxysilane. The transformation of polyamic acids into polyimides upon heating was accompanied by the formation of Si-O-Si bonds between the polymeric matrix and hydroxyl groups on zeolite surface. Secondly, the polyimide was modified using rubbery poly(dimethylsiloxane)s. Relations between film properties (i.e. interfacial adhesion and accessibility of zeolite channels for species) and film composition were studied both for unfilled and filled PI films.

Tato studie je zaměřena na přípravu porésních nosičů (keramiky, skla) a tenkých mikroporésních vrstev jako jsou zeolit nebo polyaluminium chlorid (silikalit-1, PAC). V práci je diskutována modifikace keramického nosiče na bázi Al2O3 a jeho příprava kluzovým odléváním. Byly navrženy a prověřeny optimální podmínky pro modifikaci keramických podložek za použití polyaluminium chloridu a kluzového odléváním. Druhá část práce je věnována syntéze borosilikátového skla. Jsou diskutovány výsledky charakterizování pomocí SEM a rtuťové porozimetrie a výsledky permeačních měření.