0024926 - ÚFM 2006 RIV CZ eng C - Konferenční příspěvek (zahraniční konf.)
Zemčík, L. - Dlouhý, Antonín - Król, S. - Pražmowski, M.
Vacuum metallurgy of TiAl intermetallics.
[Vakuová metalurgie intermetalik TiAl.]
Metal 2005. Ostrava: Tanger s.r.o, 2005, s. 1-11.
[Metal 2005. Hradec nad Moravicí (CZ), 24.05.2005-26.05.2005]
Grant CEP: GA ČR(CZ) GA106/04/0853
Grant ostatní: GA MŠMT(CZ) KONTAKT 55
Výzkumný záměr: CEZ:AV0Z20410507
Klíčová slova: vacuum melting * TiAl intermetallics
Kód oboru RIV: JG - Hutnictví, kovové materiály

To be able to melt successfully type gamma TiAl alloys it is absolutely necessary to solve the fundamental metallurgical problems associated with the reactions between the melt and the refractories of crucibles and ceramic moulds, with the reactions between the melt and residual gases in the furnace chamber, and with the evaporation of aluminium from the melt. The paper deals with the physico - chemical analyses of the above processes and gives their evaluation based on the results of experimental melts of the type of Ti48Al2Cr2Nb1B (at.%) obtained in vacuum induction furnace. The work also gives the results of oxidation tests for the Ti48Al2Cr2Nb1B(at.%) alloy.

Pro úspěšné tavení slitin typu gama TiAl je nezbytné vyřešit základní metalurgické problémy spojené s reakcemi mezi taveninou a žárovzdorninami kelímků a keramických forem, s reakcemi taveniny se zbytkovými plyny v komoře pece a s vypařováním hliníku z taveniny. V práci jsou uvedeny fyzikálně chemické analýzy uvedených pochodů a jejich kritické hodnocení na základě výsledků experimentálních taveb slitiny typu Ti48Al2Cr2Nb1B(at.%) prováděných ve vakuové indukční peci. V práci jsou dále uvedeny výsledky testů oxidace slitiny Ti48Al2Cr2Nb1B(at.%).