0024796 - ÚFM 2006 RIV CH eng J - Článek v odborném periodiku
Milička, Karel - Dobeš, Ferdinand
Relation between uniaxial and equi-biaxial creep and creep fracture behaviour in P91 steel.
[Vztah mezi jednoosým a dvouosým creepovým a lomovým chováním u oceli P91.]
Materials Science Forum. Roč. 482, - (2005), s. 407-410. ISSN 0255-5476.
[Materials Structure & Micromechanics of Fracture /4./. Brno, 23.06.2004-25.06.2004]
Grant CEP: GA ČR(CZ) GA106/03/1353
Výzkumný záměr: CEZ:AV0Z2041904
Klíčová slova: creep test * small punch test * equi-biaxial creep test
Kód oboru RIV: JG - Hutnictví, kovové materiály
Impakt faktor: 0.399, rok: 2005

Conventional uniaxial creep tests on massive specimens and small punch creep tests on thin discs were performed on P91 steel at temperatures from 823 to 873 K. The shapes of corresponding time dependences, i. e., creep curves and time dependence of the disc deflection, are very similar. A simple linear relationship between the applied stress in creep tests and the acting force in small punch tests leading to identical times to rupture was empirically derived. The proportionality factor reaches a value close to values observed in other creep-resistant ferritic steels.

Konvenční jednoosé creepové zkoušky na masivních vzorcích a protlačovací creepové zkoušky na tenkých discích byly provedeny na oceli P91 při teplotách od 823 do 873 K. Tvary odpovídajících časových závislostí, tj. creepových křivek a časových závislostí deflekce disku jsou velmi podobné. Empiricky byl odvozen jednoduchý lineární vztah mezi aplikovaným napětím při creepové zkoušce a působící silou při protlačovací zkoušce se stejnou dobou do lomu. Úměrnostní konstanta dosahuje hodnot blízkých hodnotám pozorovaným v jiných žárupevných feritických ocelích.