Creep resistance of single crystal superalloys CMSX-4 and CM186LC.
[Creepová odolnost monokrystalů superslitin CMSX-4 a CM186LC.]
Kovové materiály. Roč. 43, č. 1 (2005), s. 5-19. ISSN 0023-432X. E-ISSN 1338-4252
Grant CEP: GA AV ČR(CZ) 1QS200410502
Výzkumný záměr: CEZ:AV0Z20410507
Klíčová slova: creep of single crystal superalloys
Kód oboru RIV: BM - Fyzika pevných látek a magnetismus
Impakt faktor: 0.973, rok: 2005

The high resistance of single crystals of nickel-base superalloys to plastic deformation and their superior strength properties at high temperatures are mainly due to the reinforcing gamma’ precipitates. The paper deals with the properties and structures of two superalloys differing in the gamma/gamma’ morphology. The creep resistance of the 001, 011 and 111 oriented single crystals of superalloys CMSX-4 and CM186LC was compared on the basis of creep rupture curves, creep deformation curves and accompanying development of microstructures in the temperature interval 750 to 950 °C. Further, the effect of notches on creep behaviour and the origin of creep cracks were examined.

Vysoká odolnost monokrystalů superslitin vůči plastické deformaci a jejich vynikající pevnostní vlastnosti za vysokých teplot jsou dány hlavně přítomností gama' precipitátů. Článek se zabývá vlastnostmi a strukturou dvou superslitin lišících se v morfologii gama/gama'. Creepová odolnost monokrystalů superslitin CMSX-4 a CM186LC s orientací 001, 011 a 111 byla porovnána na základě stanovení creepových křivek životnosti, creepových deformačních křivek a doprovázejícího vývoje mikrostruktury v teplotním intervalu 750 - 950°C. Dále byl sledován vliv vrubů a byl zkoumán počátek creepových trhlin.