Photocatalytic degradation of bisphenol A induced by dense nanocavities inside aligned 2D-TiO2 nanostructures
- 1.
SYSNO ASEP 0503773 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Photocatalytic degradation of bisphenol A induced by dense nanocavities inside aligned 2D-TiO2 nanostructures Tvůrce(i) Bakardjieva, Snejana (UACH-T) SAI, RID, ORCID
Fajgar, Radek (UCHP-M) RID, ORCID, SAI
Jakubec, Ivo (UACH-T) SAI, RID, ORCID
Kočí, Eva (UACH-T) SAI, RID
Zhigunov, Alexander (UMCH-V) RID, ORCID
Chatzisymeon, E. (GB)
Davididou, K. (GB)Celkový počet autorů 7 Zdroj.dok. Catalysis Today. - : Elsevier - ISSN 0920-5861
Roč. 328, SI (2019), s. 189-201Poč.str. 13 s. Akce European meeting on Solar Chemistry and Photocatalysis: Environmental Applications (SPEA) /10./ Datum konání 04.06.2018 - 08.06.2018 Místo konání Almería Země ES - Španělsko Typ akce WRD Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova Freeze-drying ; Anatase TiO2 ; Nanoconfined water ; Nanocavities ; Photocatalysis ; Emerging pollutants Vědní obor RIV CA - Anorganická chemie Obor OECD Inorganic and nuclear chemistry Vědní obor RIV – spolupráce Ústav chemických procesů - Anorganická chemie
Ústav makromolekulární chemie - Makromolekulární chemieCEP GA18-15613S GA ČR - Grantová agentura ČR Způsob publikování Open access s časovým embargem (15.05.2021) Institucionální podpora UACH-T - RVO:61388980 ; UCHP-M - RVO:67985858 ; UMCH-V - RVO:61389013 UT WOS 000461462200029 EID SCOPUS 85059065818 DOI 10.1016/j.cattod.2018.12.037 Anotace The preparation of materials with aligned porosity in the nanometer range is of technological importance for a wide range of applications in molecular filtration, biomaterials and catalysis. Herein we present the advantages offered by cryo lyophilisation technique as a smart and green non-standard concept to produce dense regular polyhedral nanocavities inside the 2D TiO2 nanosheets. Hierarchical morphologies of nanocavities start to appear at temperature higher than 800 degrees C and are strongly influenced by polymorph TiO2 evolution competing reactions. The small angle X-ray scattering (SAXS) analysis confirms self-assembled 3D nanocavities with size range from 5 to 10 nm in both length and width, and depth (similar to)3.6 nm formed after realising of the confined icewater. It was found that nanocavities enhance significantly the absorption properties of TiO2 in the UV region, thereby providing a new approach to increase the photoreactivity of 2D TiO2 nanosheets. The annealed precursors containing aqueous solution of peroxo polytitanic acid (PPTA) at 800 degrees C exhibited the highest photoactivity in degrading bisphenol A (BPA) due to evenly distributed nanocavities inside single anatase TiO2 nanocrystals interconnected and aligned onto the 2D TiO2 nanosheet arrays. Pracoviště Ústav anorganické chemie Kontakt Jana Kroneislová, krone@iic.cas.cz, Tel.: 311 236 931 Rok sběru 2020 Elektronická adresa http://hdl.handle.net/11104/0295554