Acoustic emission study of high temperature deformation of Mg-Zn-Y alloys with LPSO phase
- 1.
SYSNO ASEP 0492072 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Acoustic emission study of high temperature deformation of Mg-Zn-Y alloys with LPSO phase Tvůrce(i) Fekete-Horváth, Klaudia (UJF-V) ORCID
Drozdenko, D. (CZ)
Máthis, K. (CZ)
Garcés, G. (ES)
Dobroň, P. (CZ)Celkový počet autorů 5 Zdroj.dok. Minerals, Metals and Materials Series, Magnesium Technology 2018, F7. - Les Ulis : Springer, 2018 - ISSN 2367-1181 - ISBN 978-3-319-72331-0 Rozsah stran s. 203-208 Poč.str. 6 s. Forma vydání Tištěná - P Akce International Symposium on Magnesium Technology Datum konání 11.03.2018 - 15.03.2018 Místo konání Phoenix Země US - Spojené státy americké Typ akce WRD Jazyk dok. eng - angličtina Země vyd. FR - Francie Klíč. slova acoustic emission ; high temperature ; LPSO phase ; mechanical properties ; Mg alloys Vědní obor RIV BM - Fyzika pevných látek a magnetismus Obor OECD Condensed matter physics (including formerly solid state physics, supercond.) CEP EF16_013/0001794 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Institucionální podpora UJF-V - RVO:61389005 EID SCOPUS 85042458844 DOI 10.1007/978-3-319-72332-7_32 Anotace Magnesium alloys with different content of zinc (Zn) and yttrium (Y) were extruded at an extrusion ratio of 18:1 at 350 °C. The alloying elements in both Mg alloys formed a long period stacking ordered (LPSO) phase, which during the extrusion process was elongated along the extrusion direction (ED). The magnesium matrix has bimodal character composed by fine dynamically recrystallized (DRX-ed) grains and initial coarse grains elongated along ED. Compression tests with concurrent acoustic emission (AE) measurements were performed along ED at 200, 300, and 400 °C. The deformation mechanisms and the mechanical properties at 200 °C are very similar to those obtained at ambient temperatures, i.e. in the alloy with low volume fraction of the LPSO phase (<10%) twinning controls the yielding, while in the alloy with high volume fraction of the LPSO phase (around 35%) dislocation slip and kink formation are dominant. At 300 °C the reinforcing effect of the LPSO phase is reduced and at 400 °C it is not effective anymore. Pracoviště Ústav jaderné fyziky Kontakt Markéta Sommerová, sommerova@ujf.cas.cz, Tel.: 266 173 228 Rok sběru 2019
Počet záznamů: 1