Record critical current density in bulk MgB.sub.2./sub. using carbon-coated amorphous boron with optimum sintering conditions

    1.
    SYSNO ASEP0477669
    Druh ASEPC - Konferenční příspěvek (mezinárodní konf.)
    Zařazení RIVD - Článek ve sborníku
    NázevRecord critical current density in bulk MgB2 using carbon-coated amorphous boron with optimum sintering conditions
    Tvůrce(i) Muralidhar, M. (JP)
    Higuchi, M. (JP)
    Diko, P. (SK)
    Jirsa, Miloš (FZU-D) RID, ORCID
    Murakami, M. (JP)
    Celkový počet autorů5
    Číslo článku012056
    Zdroj.dok.Journal of Physics: Conference Series, 871. - Bristol : IOP Publishing, 2017 - ISSN 1742-6588
    Rozsah strans. 1-6
    Poč.str.6 s.
    Forma vydáníTištěná - P
    AkceInternational Symposium on Superconductivity /29./, ISS 2016
    Datum konání13.12.2016 - 15.12.2016
    Místo konáníTokyo
    ZeměJP - Japonsko
    Typ akceWRD
    Jazyk dok.eng - angličtina
    Země vyd.GB - Velká Británie
    Klíč. slovaMgB2 ; bulk superconductors ; microstructure ; critical currents ; carbon coated boron
    Vědní obor RIVBM - Fyzika pevných látek a magnetismus
    Obor OECDCondensed matter physics (including formerly solid state physics, supercond.)
    Institucionální podporaFZU-D - RVO:68378271
    EID SCOPUS85027982597
    DOI10.1088/1742-6596/871/1/012056
    AnotaceWe report on the synthesis and characterization of a sintered bulk MgB2 material produced at an optimized sintering temperature with a varying content of carbon-encapsulated amorphous boron. A series of MgB2 bulks was prepared with 0%, 1.5%, 2.8%, 7.3%, 12% and 16.5% of carbon-encapsulated boron. In the samples with 12% of carbon-encapsulated boron, Mg and MgB2C2 formation was observed. Tc was around 38.4 K for the pure MgB2 and decreased with increasing carbon content up to 25 K for 16.5 % of carbon-encapsulated boron. The highest Jc values of 470 kA/cm2 and 310 kA/cm2, in the self-field and 1 T, respectively, were achieved at 20 K, in the MgB2 sample with 1.5% of carbon-encapsulated boron. It proved that the optimized sintering conditions together with the appropriate amount of the carbon-coated boron were able to bring critical current performance of bulk MgB2 material up to the level necessary for real technical applications.

    PracovištěFyzikální ústav
    KontaktKristina Potocká, potocka@fzu.cz, Tel.: 220 318 579
    Rok sběru2018
Počet záznamů: 1  

  Tyto stránky využívají soubory cookies, které usnadňují jejich prohlížení. Další informace o tom jak používáme cookies.

Přijmout všeNastaveníOdmítnout vše