Microstructure and critical current density in MgB.sub.2./sub. bulk made of 4.5 wt% carbon-coated boron

  1. 1.
    SYSNO ASEP0477618
    Druh ASEPC - Konferenční příspěvek (mezinárodní konf.)
    Zařazení RIVD - Článek ve sborníku
    NázevMicrostructure and critical current density in MgB2 bulk made of 4.5 wt% carbon-coated boron
    Tvůrce(i) Higuchi, M. (JP)
    Muralidhar, M. (JP)
    Jirsa, Miloš (FZU-D) RID, ORCID
    Murakami, M. (JP)
    Celkový počet autorů4
    Číslo článku012059
    Zdroj.dok.Journal of Physics: Conference Series, 871. - Bristol : IOP Publishing, 2017 - ISSN 1742-6588
    Rozsah strans. 1-5
    Poč.str.6 s.
    Forma vydáníTištěná - P
    AkceInternational Symposium on Superconductivity /29./, ISS 2016
    Datum konání13.12.2016 - 15.12.2016
    Místo konáníTokyo
    ZeměJP - Japonsko
    Typ akceWRD
    Jazyk dok.eng - angličtina
    Země vyd.GB - Velká Británie
    Klíč. slovaMgB2 ; bulk superconductors ; microstructure ; critical currents ; carbon coated boron
    Vědní obor RIVBM - Fyzika pevných látek a magnetismus
    Obor OECDCondensed matter physics (including formerly solid state physics, supercond.)
    Institucionální podporaFZU-D - RVO:68378271
    EID SCOPUS85027998380
    DOI10.1088/1742-6596/871/1/012059
    AnotaceSuperconducting performance and its uniformity was studied in the single-step sintered MgB2 bulk prepared with 4.5 wt% of carbon in the carbon-encapsulated boron. The 20 mm in diameter MgB2 pellet was cut into several pieces from bottom to top and the microstructure, superconducting transition temperature (Tc onset), and critical current density at 20 K were studied. DC magnetization measurements showed a sharp superconducting transition with onset Tc at around 35.5 K in all positions. SEM analysis indicated a dispersion of grains between 200 and 300 nm in size, as the main pinning medium in this MgB2 superconductors. The critical current density at 20 K was quite uniform, around 330 kA/cm2 and 200 kA/cm2 at self-field and 1 T, respectively, for all measured positions. The results indicate that the carbonencapsulated boron is very promising for production of high quality bulk MgB2 material for various industrial applications.
    PracovištěFyzikální ústav
    KontaktKristina Potocká, potocka@fzu.cz, Tel.: 220 318 579
    Rok sběru2018
Počet záznamů: 1  

  Tyto stránky využívají soubory cookies, které usnadňují jejich prohlížení. Další informace o tom jak používáme cookies.