Thermal behavior of an intumescent alkaline aluminosilicate composite material for fire protection of structural elements

SYSNO ASEP	0496983
Druh ASEP	J - Článek v odborném periodiku
Zařazení RIV	J - Článek v odborném periodiku
Poddruh J	Článek ve WOS
Název	Thermal behavior of an intumescent alkaline aluminosilicate composite material for fire protection of structural elements
Tvůrce(i)	Sotiriadis, Konstantinos (UTAM-F)_{RID, ORCID, SAI} Guzii, S. (UA) Mácová, Petra (UTAM-F)_{RID, SAI, ORCID} Viani, Alberto (UTAM-F)_{RID, ORCID, SAI} Dvořák, K. (CZ) Drdácký, Miloš (UTAM-F)_{RID, SAI, ORCID}
Celkový počet autorů	6
Číslo článku	04019058
Zdroj.dok.	Journal of Materials in Civil Engineering. - : American Society of Civil Engineers - ISSN 0899-1561 Roč. 31, č. 6 (2019)
Poč.str.	9 s.
Forma vydání	Tištěná - P
Jazyk dok.	eng - angličtina
Země vyd.	US - Spojené státy americké
Klíč. slova	alkaline aluminosilicate materials ; metakaolin ; intumescent coatings ; fire protection ; X-ray micro-computed tomography
Vědní obor RIV	JN - Stavebnictví
Obor OECD	Construction engineering, Municipal and structural engineering
CEP	GBP105/12/G059 GA ČR - Grantová agentura ČR
Způsob publikování	Omezený přístup
Institucionální podpora	UTAM-F - RVO:68378297
UT WOS	000461616400001
EID SCOPUS	85063142428
DOI	10.1061/(ASCE)MT.1943-5533.0002702
Anotace	The behavior of a composite material, consisting of metakaolin-based alkaline aluminosilicate binder, granules of the same initial composition used as a swelling agent, and calcium carbonate, was studied during firing in the temperature range 25°C–1,000°C. A combination of techniques was used to investigate its microstructure, composition, and properties. The material developed porosity at 200°C, largely contributed by water loss from the swelling agent, resulting in expansion and decrease in thermal conductivity and mechanical strength. Between 400°C and 800°C the thermal insulation characteristics further improved. At 1,000°C, crystallization of new phases with a decrease in the amorphous content produced a small contraction and increased thermal conductivity and mechanical strength. The material exhibited good stability with appropriate characteristics for use as intumescent coating for fire protection of structural elements. Modification of the binder:granules ratio may allow producing composites for specific applications.
Pracoviště	Ústav teoretické a aplikované mechaniky
Kontakt	Kulawiecová Kateřina, kulawiecova@itam.cas.cz, Tel.: 225 443 285
Rok sběru	2019
Elektronická adresa	https://doi.org/10.1061/(ASCE)MT.1943-5533.0002702

Počet záznamů: 1