Thermal behavior of an intumescent alkaline aluminosilicate composite material for fire protection of structural elements

0496983 - ÚTAM 2019 RIV US eng J - Článek v odborném periodiku
Sotiriadis, Konstantinos - Guzii, S. - Mácová, Petra - Viani, Alberto - Dvořák, K. - Drdácký, Miloš
Thermal behavior of an intumescent alkaline aluminosilicate composite material for fire protection of structural elements.
Journal of Materials in Civil Engineering. Roč. 31, č. 6 (2019), č. článku 04019058. ISSN 0899-1561. E-ISSN 1943-5533
Grant CEP: GA ČR(CZ) GBP105/12/G059
Institucionální podpora: RVO:68378297
Klíčová slova: alkaline aluminosilicate materials * metakaolin * intumescent coatings * fire protection * X-ray micro-computed tomography
Obor OECD: Construction engineering, Municipal and structural engineering
Impakt faktor: 2.169, rok: 2019
Způsob publikování: Omezený přístup
https://doi.org/10.1061/(ASCE)MT.1943-5533.0002702

The behavior of a composite material, consisting of metakaolin-based alkaline aluminosilicate binder, granules of the same initial composition used as a swelling agent, and calcium carbonate, was studied during firing in the temperature range 25°C–1,000°C. A combination of techniques was used to investigate its microstructure, composition, and properties. The material developed porosity at 200°C, largely contributed by water loss from the swelling agent, resulting in expansion and decrease in thermal conductivity and mechanical strength. Between 400°C and 800°C the thermal insulation characteristics further improved. At 1,000°C, crystallization of new phases with a decrease in the amorphous content produced a small contraction and increased thermal conductivity and mechanical strength. The material exhibited good stability with appropriate characteristics for use as intumescent coating for fire protection of structural elements. Modification of the binder:granules ratio may allow producing composites for specific applications.